Efficacy of application of zinc oxide on the surface of the NiO/Al 2O3 catalytic systemEfficacy of application of zinc oxide on the surface of the NiO/Al 2O3 catalytic system
Efficacy of application of zinc oxide on the surface of the NiO/Al 2O3 catalytic system
 
الموضوع : كيمياء 
لغة الوثيقة : الانجليزية 
المستخلص : The surface and catalytic properties of the NiO/Al2O3 system after deposition of 3 to 7% zinc oxide on its surface and heat treatment at 400, 600, and 800°C were investigated by X-ray diffraction analysis, nitrogen adsorption at -196°C, and catalytic oxidation of carbon monoxide by oxygen at 150-250°C. It was shown that calcination of the catalyst at 400°C decreases the specific surface area, while it increases it at 600 and 800°C. The decrease in the specific surface area is accompanied by an increase in the size of the NiO/Al2O3 crystallites. The activity of the catalysts calcined at 400°C in oxidation of carbon monoxide by oxygen, manifested by a constant reaction rate, increases with an increase in the zinc oxide content on the surface. After deposition of the zinc oxide, the mechanism of the oxidation reaction remains as before, but the concentration of active centers in the catalyst changes. 
ردمد : 0009-3092 
اسم الدورية : Chemistry and Technology of Fuels and Oils 
المجلد : 47 
العدد : 1 
سنة النشر : 1432 هـ
2011 م 
نوع المقالة : مقالة علمية 
تاريخ الاضافة على الموقع : Tuesday, September 20, 2011 

الباحثون

اسم الباحث (عربي)اسم الباحث (انجليزي)نوع الباحثالمرتبة العلميةالبريد الالكتروني
السيد البدوي المسلميEl-Mossalamy, El-sayed El-Badawy باحثدكتوراهsbdmina@yahoo.com
سليمان ناصر باسهلBasahel, Suliman Naserباحثدكتوراهsbasahel@kau.edu.sa
عبدالله يوسف عبيدObaid, Abdullah Yousifباحثدكتوراهaobaid@kau.edu.sa

الملفات

اسم الملفالنوعالوصف
 30517.pdf pdfAbstract

الرجوع إلى صفحة الأبحاث