Characterization of Se88Te12 nanostructured chalcogenide prepared by ball milling
Characterization of Se88Te12 nanostructured chalcogenide prepared by ball milling
 
الموضوع : فيزياء 
لغة الوثيقة : الانجليزية 
المستخلص : The present work deals with the structural and optical studies of Se88Te12 chalcogenide nanoparticles prepared by ball milling. Polycrystalline Se88Te12 chalcogenide prepared by melt quenching was used as a starting material. The ball milling was performed in a Laboratory 8000 M-Mixer/Mill (SPEX) mill using hardened steel balls and a vial with a ball-to-powder weight ratio of 10:1. After various times of milling, a small amount of material was taken from the container to be characterized by Transmission Electron Microscopy and optical measurements in thin film form within the wavelength region 400-1000 nm. Optical absorption measurements indicate that the absorption mechanism is due to direct transition. It has been observed that the optical band gap increases with the increase of milling time. The results are interpreted in terms of the change in concentration of localized states due to the shift in Fermi level. 
ردمد : 0167-577X 
اسم الدورية : Materials Letters 
المجلد : 64 
العدد : 12 
سنة النشر : 1431 هـ
2010 م 
نوع المقالة : مقالة علمية 
تاريخ الاضافة على الموقع : Sunday, October 16, 2011 

الباحثون

اسم الباحث (عربي)اسم الباحث (انجليزي)نوع الباحثالمرتبة العلميةالبريد الالكتروني
شمشاد أحمد خانKhan, Shamshad Ahmedباحثدكتوراهshamshad_phys@yahoo.com
فيصل عبدالعزيز العقلAl-Agel, Faisal Aباحثدكتوراهfagel@kau.edu.sa
عادل صالح فيدةFaidah, Adel Sباحثدكتوراهafaidah@kau.edu.sa
سعود جميل يغمورYaghmour, Saud Jameelباحثدكتوراهsyaghmour@kau.edu.sa
أحمد عبدالله الغامديAl-Ghamdi, A AباحثدكتوراهAGAMDI@kau.edu.sa

الرجوع إلى صفحة الأبحاث